Weili REN
,
Jianting GUO
,
Gusong LI
,
Jiyang ZHOU
材料科学技术（英）
The influence of strain rate and temperature on the tensile behavior of as-cast and HIPed NiAl-9Mo eutectic alloy was investigated in the temperature range of 700~950℃ and over a strain rate range from 2.08×10-4 s-1 to 2.08×10-2 s-1. The results indicate that HIP process causes an enhancement in ductility and a decrease in ultimate tensile strength (UTS), yield strength (YS), average strain hardening rate as well as a drop in brittle to ductile transition temperature(BDTT) under the same condition. It is noticed that the BDTT of as-cast NiAl-9Mo is more dependent on strain rate than that of HIPed one. The brittle to ductile transition process of the alloy is related to a sharp drop in strain hardening rate. Regardless of strain rate, the fracture morphology changes from cleavage in NiAl phase and debonding along NiAl/Mo interface below the BDTT to microvoid coalescence above BDTT. The apparent activation energy of the BDT of HIPed and as-cast material are calculated to be 327 and 263 kJ/mol, respectively, suggesting that the mechanism is associated with lattice diffusion in NiAl phase.
关键词:
NiAl-9Mo
,
null
,
null
,
null
Jianbo YU
,
Zhongming REN
,
Weili REN
,
Kang DENG
,
Yunbo ZHONG
金属学报(英文版)
doi:10.1016/S1006-7191(08)60088-5
An electromagnetic vibration was generated by simultaneously imposing a strong static magnetic field (up to 10 T) and an alternative electricity current to the metal. Its effects on the solidification structure of eutectic Al-Si alloy have been investigated experimentally. It is found that the eutectic structure has been refined by solely imposing high magnetic field while it is coarsened under the electromagnetic vibration. Furthermore, polyhedral Si grains and non-dendritic α-Al appeared when the electromagnetic vibration strength was strong enough. The refining of eutectic structure is attributed to the decrease of diffusion coefficient caused by the strong magnetic field. The coarseness of eutectic structure may be attributed to the convection caused by electromagnetic vibration. Strong convection may break co-operative growth of eutectic phases to form polyhedral Si grains and non-dendritic α-Al.
关键词:
Strong magnetic field
,
null
,
null
,
null
,
null